TPU煙臺美瑞E190L原料物性介紹

總體  
材料狀態  •已商用：當前有效
 
資料 1  •Brochure - Product description (Japanese)
 •Processing (Japanese)
 •Technical Datasheet - data table (Japanese)
 
 
供貨地區  •亞太地區
 
性能特點  •減震
•抗撞擊性，良好
•良好的強度
•良好的柔韌性
 •良好的撕裂強度
•耐臭氧性能
•耐低溫
•耐化學性良好
 •耐磨損性良好
•耐氣候影響性能良好
•耐油性能
 
 

物理性能 額定值 單位制 測試方法
比重 1.22 g/cm³ ASTM D792
硬度 額定值 單位制 測試方法
硬度計硬度 (邵氏 A, 23°C, 2.00 mm, 注塑) 88 到 92   ASTM D2240

機械性能 額定值 單位制 測試方法
抗泰伯磨耗 (23°C, 1000 Cycles, 1000 g, H-22 轉輪) 35.0 mg ASTM D1044
彈性體 額定值 單位制 測試方法
拉伸應力 2 (100%應變, 23°C, 2.00 mm) 10.0 MPa ASTM D412
抗張強度 2 (屈服, 23°C, 2.00 mm) 46.0 MPa ASTM D412
伸長率 2 (斷裂, 23°C, 2.00 mm) 580 % ASTM D412
撕裂強度 2 (23°C, 2.00 mm) 137 kN/m ASTM D624
壓縮永久變形 (70°C, 22.0 hr) 32 % ASTM D395
Rebound Resilience (23°C, 2.00 mm) 45 %  

熱性能 額定值 單位制 測試方法
玻璃轉化溫度(DSC) -43.0 °C DSC
維卡軟化溫度 118 °C ASTM D1525 3

補充信息
Test Methods: JIS K7311, K6262, K7206

General  
Material Status  •Commercial: Active

Availability  •Asia Pacific
 
Features  •Good Chemical Resistance
•Good Flexibility
•Good Impact Resistance
•Good Strength
 •Good Tear Strength
•Good Wear Resistance
•Good Weather Resistance
•Low Temperature Resistant
 •Oil Resistant
•Ozone Resistant
•Vibration Damping
 

Physical Nominal Value Unit Test Method
Specific Gravity 1.22 g/cm³ ASTM D792
Hardness Nominal Value Unit Test Method
Durometer Hardness (Shore A, 23°C, 2.00 mm, Injection Molded) 88 to 92   ASTM D2240

Mechanical Nominal Value Unit Test Method
Taber Abrasion Resistance (23°C, 1000 Cycles, 1000 g, H-22 Wheel) 35.0 mg ASTM D1044
Elastomers Nominal Value Unit Test Method
Tensile Stress 2 (100% Strain, 23°C, 2.00 mm) 10.0 MPa ASTM D412
Tensile Strength 2 (Yield, 23°C, 2.00 mm) 46.0 MPa ASTM D412
Tensile Elongation 2 (Break, 23°C, 2.00 mm) 580 % ASTM D412
Tear Strength 2 (23°C, 2.00 mm) 137 kN/m ASTM D624
Compression Set (70°C, 22.0 hr) 32 % ASTM D395
Rebound Resilience (23°C, 2.00 mm) 45 %  

Thermal Nominal Value Unit Test Method
Glass Transition Temperature (DSC) -43.0 °C DSC
Vicat Softening Temperature 118 °C ASTM D1525 3

Additional Information
Test Methods: JIS K7311, K6262, K7206